Ефект на напредната технологија врз услужниот живот на челик отпорен на топлина

The characteristics of the morphology and distribution of inclusions, grain thickness and brittle phase, and the role of chemical composition, metamorphic treatment, heat treatment and metal pouring of ZG0Cr23Ni13 heat-resistant steel were studied. After complex tests, data statistics and comparison, it can be concluded that compound metamorphism treatment, metal pouring, solid treatment and vacuum melting and other advanced technology are different℃to improve the mechanical properties of room temperature, high temperature and heat resistance fatigue performance, which is attributed to the refinement of grains, the elimination of mesh and the improvement of inclusion form and distribution. For metal materials, using different heat treatment processes will affect the tissue structure and grain size, thus changing the difficulty of their thermal activation Движење . Во анализата на неуспехот на кастинг, има многу фактори што доведуваат до неуспех, главно термички замор што доведува до ртење на пукнатини и развој . Соодветно, постојат серија фактори кои влијаат на иницијацијата и проширувањето на пукнатините, меѓу кои, меѓу сулфур содржината е исклучително важна, затоа што пукнатините се развиваат во врска со ’ sulfur content is affected by raw materials and their smelting quality, if the castings working under the protective atmosphere of hydrogen, hydrogen sulfide in hydrogen will cause the casting to permeate sulfur. Secondly, the adequacy of the solid solution treatment will affect the strong toughness of the casting.